Biodegradable ferroelectric molecular crystal with large piezoelectric response.

Transient implantable piezoelectric materials are desirable for biosensing, drug delivery, tissue regeneration, and antimicrobial and tumor therapy. For use in the human body, they must show flexibility, biocompatibility, and biodegradability. These requirements are challenging for conventional inorganic piezoelectric oxides and piezoelectric polymers. We discovered high piezoelectricity in a molecular crystal HOCH2(CF2)3CH2OH [2,2,3,3,4,4-hexafluoropentane-1,5-diol (HFPD)] with a large piezoelectric coefficient d33 of ~138 picocoulombs per newton and piezoelectric voltage constant g33 of ~2450 × 10-3 volt-meters per newton under no poling conditions, which also exhibits good biocompatibility toward biological cells and desirable biodegradation and biosafety in physiological environments. HFPD can be composite with polyvinyl alcohol to form flexible piezoelectric films with a d33 of 34.3 picocoulombs per newton. Our material demonstrates the ability for molecular crystals to have attractive piezoelectric properties and should be of interest for applications in transient implantable electromechanical devices.

Modulating the ferroelectric phases in cholesteryl-based organic compounds with perfluoroalkyl tail engineering.

Here, we synthesized a series of cholesteryl-based compounds, whose phases and their transformation can be modulated by temperature and the chain length of the fluoroalkyl moieties. To our knowledge, this is the first time that the phase transition could be modulated with perfluoroalkyl tail engineering in organic single-component ferroelectric crystals.

Association between type 2 diabetes mellitus and body composition based on MRI fat fraction mapping.

Purpose: To explore the association between type 2 diabetes mellitus (T2DM) and body composition based on magnetic resonance fat fraction (FF) mapping. Methods: A total of 341 subjects, who underwent abdominal MRI examination with FF mapping were enrolled in this study, including 68 T2DM patients and 273 non-T2DM patients. The FFs and areas of visceral adipose tissue (VAT), subcutaneous adipose tissue (SAT) and abdominal muscle (AM) were measured at the level of the L1-L2 vertebral. The FF of bone marrow adipose tissue (BMAT) was determined by the averaged FF values measured at the level of T12 and L1 vertebral, respectively. The whole hepatic fat fraction (HFF) and pancreatic fat fraction (PFF) were measured based on 3D semi-automatic segmentation on the FF mapping. All data were analyzed by GraphPad Prism and MedCalc. Results: VAT area, VAT FF, HFF, PFF of T2DM group were higher than those of non-T2DM group after adjusting for age and sex (P < 0.05). However, there was no differences in SAT area, SAT FF, BMAT FF, AM area and AM FF between the two groups (P > 0.05). VAT area and PFF were independent risk factors of T2DM (all P < 0.05). The area under the curve (AUC) of the receiver operating characteristic (ROC) for VAT area and PFF in differentiating between T2DM and non-T2DM were 0.685 and 0.787, respectively, and the AUC of PFF was higher than VAT area (P < 0.05). Additionally, in seemingly healthy individuals, the SAT area, VAT area, and AM area were found to be significantly associated with being overweight and/or obese (BMI ≥ 25) (all P < 0.05). Conclusions: In this study, it was found that there were significant associations between T2DM and VAT area, VAT FF, HFF and PFF. In addition, VAT area and PFF were the independent risk factors of T2DM. Especially, PFF showed a high diagnostic performance in discrimination between T2DM and non-T2DM. These findings may highlight the crucial role of PFF in the pathophysiology of T2DM, and it might be served as a potential imaging biomarker of the prevention and treatment of T2DM. Additionally, in individuals without diabetes, focusing on SAT area, VAT area and AM area may help identify potential health risks and provide a basis for targeted weight management and prevention measures.

Observation of Ferroelectric Lithography on Biodegradable PLA Films.

Ferroelectric lithography, which can purposefully control and pattern ferroelectric domains in the micro-/nanometer scale, has extensive applications in data memories, field-effect transistors, race-track memory, tunneling barriers, and integrated biochemical sensors. In pursuit of mechanical flexibility and light weight, organic ferroelectric polymers such as poly(vinylidene fluoride) are developed; however, they still suffer from complicated stretching processes of film fabrication and poor degradability. These poor features severely hinder their applications. Here, the ferroelectric lithography on the biocompatible and biodegradable poly(lactic acid) (PLA) thin films at room temperature is demonstrated. The semicrystalline PLA thin film can be easily fabricated through the melt-casting method, and the desired domain structures can be precisely written according to the predefined patterns. Most importantly, the coercive voltage (Vc ) of PLA thin film is relatively low (lower than 30 V) and can be further reduced with the decrease of the film thickness. These intriguing behaviors combined with satisfying biodegradability make PLA thin film a desirable candidate for ferroelectric lithography and enable its future application in the field of bioelectronics and biomedicine. This work sheds light on further exploration of ferroelectric lithography on other polymer ferroelectrics as well as their application as nanostructured devices.

Organic radical ferroelectric crystals with martensitic phase transition.

Organic martensitic compounds are an emerging type of smart material with intriguing physical properties including thermosalient effect, ferroelasticity, and shape memory effect. However, due to the high structural symmetry and limited design theories for these materials, the combination of ferroelectricity and martensitic transformation has rarely been found in organic systems. Here, based on the chemical design strategies for molecular ferroelectrics, we show a series of asymmetric 1,4,5,8-naphthalenediimide derivatives with the homochiral amine and 2,2,6,6-tetramethylpiperidine-N-oxyl components, which adopt the low-symmetric polar structure and so allow ferroelectricity. Upon H/F substitution, the fluorinated compounds exhibit reversible ferroelectric and martensitic transitions at 399 K accompanied by a large thermal hysteresis of 132 K. This large thermal hysteresis with two competing (meta)-stable phases is further confirmed by density functional theory calculations. The rare combination of martensitic phase transition and ferroelectricity realizes the bistability with two different ferroelectric phases at room temperature. Our finding provides insight into the exploration of martensitic ferroelectric compounds with potential applications in switchable memory devices, soft robotics, and smart actuators.

Ferroelectric polymers take a step toward bioelectronics.

Chemical modification opens new applications for polymers in wearables.

Ferroelectric Phase Transition Driven by Switchable Covalent Bonds.

The mechanism on ferroelectric phase transitions is mainly attributed to the displacive and/or order-disorder transition of internal components since the discovery of the ferroelectricity in 1920, rather than the breaking and recombination of chemical bonds. Here, we demonstrate how to utilize the chemical bond rearrangement in a diarylethene-based crystal to realize the light-driven mm2F1-type ferroelectric phase transition. Such a photoinduced phase transition is entirely driven by switchable covalent bonds with breaking and reformation, enabling the reversible light-controllable ferroelectric polarization switching, dielectric and nonlinear optical bistability. Moreover, light as quantized energy can achieve contactless, nondestructive, and remote-control operations. This work proposes a new mechanism of ferroelectric phase transition, and highlights the significance of photochromic molecules in designing new ferroelectrics for photocontrol data storage and sensing.

High-T c Single-Component Organosilicon Ferroelectric Crystal Obtained by H/F Substitution.

Organic single-component ferroelectrics are highly desirable for their low molecular mass, light weight, low processing temperature, and excellent film-forming properties. Organosilicon materials with a strong film-forming ability, weather resistance, nontoxicity, odorlessness, and physiological inertia are very suitable for device applications related to the human body. However, the discovery of high-T c organic single-component ferroelectrics has been very scarce, and the organosilicon ones even less so. Here, we used a chemical design strategy of H/F substitution to successfully synthesize a single-component organosilicon ferroelectric tetrakis(4-fluorophenylethynyl)silane (TFPES). Systematic characterizations and theory calculations revealed that, compared with the parent nonferroelectric tetrakis(phenylethynyl)silane, fluorination caused slight modifications of the lattice environment and intermolecular interactions, inducing a 4/mmmFmm2-type ferroelectric phase transition at a high T c of 475 K in TFPES. To our knowledge, this T c should be the highest among the reported organic single-component ferroelectrics, providing a wide operating temperature range for ferroelectrics. Moreover, fluorination also brought about a significant improvement in the piezoelectric performance. Combined with excellent film properties, the discovery of TFPES provides an efficient path for designing ferroelectrics suitable for biomedical and flexible electronic devices.

Three-dimensional narrow-bandgap perovskite semiconductor ferroelectric methylphosphonium tin triiodide for potential photovoltaic application.

A novel A-site three-dimensional organic-inorganic halide perovskites (3D OIHP) ferroelectric, methylphosphonium tin triiodide (MPSnI3), featuring a narrow bandgap of 1.43 eV, was synthesized. The integration of ferroelectricity with initially moderate efficiency (2.23%) may afford a promising platform to investigate the ferroelectric photovoltaic effect in organic-inorganic halide perovskite solar cells.

A Poling-Free Supramolecular Crown Ether Compound with Large Piezoelectricity.

Supramolecular host-guest ferroelectrics based on solution processing are highly desirable because they are generally created with intrinsic piezoelectricity/ferroelectricity and do not need further poling. Poly(vinylidene fluoride) (PVDF) in the electric-active beta phase after stretching/annealing still shows no piezoelectric response unless poled. Although many supramolecular host-guest ferroelectrics have been discovered, their piezoelectricity is relatively small. Based on H/F substitution, we reported a supramolecular host-guest compound [(CF3-C6H4-NH3)(18-crown-6)][TFSA] (CF3-C6H4-NH3 = 4-trifluoromethylanilinium, TFSA = bis(trifluoromethanesulfonyl)ammonium) with a remarkable piezoelectric response of 42 pC/N under no poling condition. The introduction of F atoms increases phase transition temperature, polar axes, second harmonic generation (SHG) intensity, and piezoelectric coefficient d33. To our knowledge, such a large piezoelectric performance of [(CF3-C6H4-NH3)(18-crown-6)][TFSA] makes its d33, piezoelectric voltage coefficient g33, and mechanical quality factor Qm the highest among the reported supramolecular host-guest ferroelectric compounds and even larger than the values of PVDF. This work provides inspiration for optimizing piezoelectricity on molecular materials.

Sleep benefit in patients with Parkinson's disease is associated with the dopamine transporter expression in putamen.

PURPOSE: Sleep benefit (SB) is a well-known phenomenon in patients with Parkinson's disease (PD); however, the mechanisms underlying this phenomenon remain unclear. This study aimed to evaluate whether the SB phenomenon in PD patients is associated with dopamine transporter (DAT) expression levels in the striatum. METHODS: The data of 125 PD patients were collected and divided into SB (n = 61) and non-SB (nSB) groups (n = 54) depending on whether they had SB or not. DAT expression on both sides of the striatum in PD patients was measured using 2b-carbomethoxy-3b-(4-trimethylstannylphenyl) tropane (11C-CFT) positron emission tomography imaging. The clinical variables, sleep scores, and striatum 11C-CFT uptake index of PD patients between the SB and nSB groups were compared. The associations of clinical variables, sleep scores, and striatum 11C-CFT uptake index with the SB variable were analyzed using logistic regression analysis. A receiver operating characteristic (ROC) curve was used to evaluate the diagnostic value of the striatum 11C-CFT uptake index in distinguishing SB patients from nSB patients. RESULTS: The tremor subtype ratio (P = 0.011), levodopa equivalent daily dose (LEDD) (P < 0.001), sleep efficiency score (P = 0.025), habitual sleep efficiency (P = 0.012), and night sleep duration (P = 0.005) in the SB group were significantly different from those in the nSB group. The 11C-CFT uptake index in both the contralateral and ipsilateral striata in the SB group was significantly higher than that in the nSB group (P < 0.05). The binary logistic regression showed that SB variables were significantly and independently associated with tremor subtype (P = 0.048), LEDD (P = 0.021), sleep duration at night (P = 0.035), 11C-CFT uptake index in the contralateral (P = 0.013) and ipsilateral (P = 0.019) putamen in PD patients after correction for important clinical confounders. ROC analysis showed that the 11C-CFT uptake index on the onset side of the putamen had a high capacity (AUC: 0.916) to distinguish SB patients from nSB patients with high sensitivity (83.33 %) and specificity (88.89 %). CONCLUSION: DAT expression in the putamen was associated with the SB phenomenon in PD patients, and the putamen DAT expression level could predict the SB phenomenon in PD patients.

Axial-Chiral BINOL Multiferroic Crystals with Coexistence of Ferroelectricity and Ferroelasticity.

Chirality exists everywhere from natural amino acids to particle physics. The introduction of point chirality has recently been shown to be an efficient strategy for the construction of molecular ferroelectrics. In contrast to point chirality, however, axial chirality is rarely used to design ferroelectrics so far. Here, based on optically active 1,1'-bi-2-naphthol (BINOL), which has been applied extensively as a versatile chiral reagent in asymmetric catalysis, chiral recognition, and optics, we successfully design a pair of axial-chiral BINOL multiferroics, (R)-BINOL-DIPASi and (S)-BINOL-DIPASi. They experience a 2F1-type full ferroelectric/ferroelastic phase transition at a high temperature of 362 and 363 K, respectively. Piezoelectric force microscopy and polarization-voltage hysteresis loops demonstrate their ferroelectric domains and domain switching, and polarized light microscopy visualizes the evolution of stripe-shaped ferroelastic domains. The axial-chiral BINOL building block promotes the generation of the polar structure and ferroelectricity, and the organosilicon component increases the rotational energy barrier and thus the phase transition temperature. This work presents the first axial-chiral high-temperature multiferroic crystals, offering an efficient path for designing molecular multiferroics through the introduction of axial chirality.

The First Chiro-Inositol Organosilicon Ferroelectric Crystal.

Organosilicons have been used extensively in aerospace, electronics, food, medicine and other fields, due to their low viscosity, hydrophobicity, corrosion resistance, non-toxic, and physiologically inert features. Despite extensive interest, however, organosilicon ferroelectric crystals have never been found. Here, by using the chemical design strategy, we successfully obtained a molecular ferroelectric D-chiro-inositol-SiMe3 with polar P43 symmetry, whose spontaneous polarization can be electrically switchable on thin film. The introduction of organosilicon groups endows the thin films with excellent softness, ductility and flexibility (extremely low hardness of 72.8 MPa and small elastic modulus of 5.04 GPa) that are desirable for biomedical and human-compatible applications. As the first case of organosilicon ferroelectric crystal to date, this work offers a new structural paradigm for molecular ferroelectrics, and highlights their potential for flexible bio-electronic applications.

A small-molecule organic ferroelectric with piezoelectric voltage coefficient larger than that of lead zirconate titanate and polyvinylidene difluoride.

Piezoelectric materials that generate electricity when deforming are ideal for many implantable medical sensing devices. In modern piezoelectric materials, inorganic ceramics and polymers are two important branches, represented by lead zirconate titanate (PZT) and polyvinylidene difluoride (PVDF). However, PVDF is a nondegradable plastic with poor crystallinity and a large coercive field, and PZT suffers from high sintering temperature and toxic heavy element. Here, we successfully design a metal-free small-molecule ferroelectric, 3,3-difluorocyclobutanammonium hydrochloride ((3,3-DFCBA)Cl), which has high piezoelectric voltage coefficients g 33 (437.2 × 10-3 V m N-1) and g 31 (586.2 × 10-3 V m N-1), a large electrostriction coefficient Q 33 (about 4.29 m4 C-2) and low acoustic impedance z 0 (2.25 × 106 kg s-1 m-2), significantly outperforming PZT (g 33 = 34 × 10-3 V m N-1 and z 0 = 2.54 × 107 kg s-1 m-2) and PVDF (g 33 = 286.7 × 10-3 V m N-1, g 31 = 185.9 × 10-3 V m N-1, Q 33 = 1.3 m4 C-2, and z 0 = 3.69 × 106 kg s-1 m-2). Such a low acoustic impedance matches that of the body (1.38-1.99 × 106 kg s-1 m-2) reasonably well, making it attractive as next-generation biocompatible piezoelectric devices for health monitoring and "disposable" invasive medical ultrasound imaging.

Enantioselective Pd-catalyzed dearomative reductive Heck and domino Heck-Suzuki reactions of 2-CF3-indoles.

Highly enantioselective palladium-catalyzed dearomative reductive Heck reaction and domino Heck-Suzuki reaction of 2-CF3-indoles have been developed. Using Pd(OAc)2/(R)-Synphos as the catalyst and Et3SiH as a hydride source, a variety of indolines bearing a 2-trifluoromethyl quaternary stereocenter were obtained via a dearomative reductive Heck reaction. Alternatively, using Pd(dba)2/phosphoramidite as the catalyst and Ar4BNa as a coupling partner, structurally diverse indolines containing two vicinal carbon stereocenters were afforded through the domino dearomative Heck-Suzuki reaction.

Solvent Selective Effect Occurs in Iodinated Adamantanone Ferroelectrics.

Organic ferroelectrics, as a type of crystalline compound, are generally solution processing. However, for most crystalline compounds, the changing of solvent would not influence the crystalline phase, let alone their physical performance. Here, the solvent selective effect occurs in the iodinated adamantanone ferroelectrics. By changing the solvent with different polarities, the ferroelectric crystals can be induced in two different phases, which is unprecedented to the knowledge. More strikingly, this solvent-induced transformation could realize the physical performance optimization in the orthorhombic phase (orth-I-OA, obtained from ethanol) with a stronger second harmonic generation (SHG) response, greater piezoelectric coefficient d33 of 5 pC N-1 , and larger spontaneous polarization (Ps ) of 3.43 µC cm-2 than those of monoclinic one (mono-I-OA, obtained from ethyl acetate). Such an intriguing phenomenon might be closely related to solvent polarity. Based on the quantitative and qualitative analyses, the similar interaction energies of these two phases suggest that their transformation could be easily realized via changing the solvent. This work provides new insights into the chemical design and performance optimization of organic ferroelectrics.

[(Histamine)(18-crown-6)2][BF4]2 is a high-temperature piezoelectric.

We discovered that [(histamine)(18-crown-6)2][BF4]2 is a high-temperature host-guest inclusion complex that presents decent piezoelectric properties (d33 = 5 pC/N), undergoes a phase transition at 406 K, and also possesses potential ferroelectricity. This work provides a new idea for constructing host-guest inclusion piezoelectrics.

Ferroelectric Lithography in Single-Component Organic Enantiomorphic Ferroelectrics.

Organic ferroelectrics are flexible, lightweight, and bio-friendly, promising for bio-harmonized electronic devices, while their ferroelectric lithography remains relatively unexplored. Here, by introducing homochirality and ZE photoisomerization, we obtained a pair of organic enantiomorphic ferroelectrics, di(benzylamino)-substituted derivatives of muconic acids, the first ferroelectrics in the muconic family. Their ferroelectric and chiral features were confirmed by the polarization-electric field hysteresis loops and circular dichroism spectra, respectively. Piezoresponse force microscopy measurements demonstrate that the desired domain structure can be precisely achieved by applying a local electric field on a predefined pattern in their thin films. Moreover, thermogravimetric analyses reveal that their ferroelectricity can persist up to above 550 K. The precise pattern lithography and excellent thermal stability make them competitive candidates for ferroelectric lithography.

PFM (piezoresponse force microscopy)-aided design for molecular ferroelectrics.

With prosperity, decay, and another spring, molecular ferroelectrics have passed a hundred years since Valasek first discovered ferroelectricity in the molecular compound Rochelle salt. Recently, the proposal of ferroelectrochemistry has injected new vigor into this century-old research field. It should be highlighted that piezoresponse force microscopy (PFM) technique, as a non-destructive imaging and manipulation method for ferroelectric domains at the nanoscale, can significantly speed up the design rate of molecular ferroelectrics as well as enhance the ferroelectric and piezoelectric performances relying on domain engineering. Herein, we provide a brief review of the contribution of the PFM technique toward assisting the design and performance optimization of molecular ferroelectrics. Relying on the relationship between ferroelectric domains and crystallography, together with other physical characteristics such as domain switching and piezoelectricity, we believe that the PFM technique can be effectively applied to assist the design of high-performance molecular ferroelectrics equipped with multifunctionality, and thereby facilitate their practical utilization in optics, electronics, magnetics, thermotics, and mechanics among others.

Record Enhancement of Curie Temperature in Host-Guest Inclusion Ferroelectrics.

Solid-state molecular rotor-type materials such as host-guest inclusion compounds are very desirable for the construction of molecular ferroelectrics. However, they usually have a low Curie temperature (Tc) and uniaxial nature, severely hindering their practical applications. Herein, by regulating the anion to control "momentum matching" in the crystal structure, we successfully designed a high-temperature multiaxial host-guest inclusion ferroelectric [(MeO-C6H4-NH3)(18-crown-6)][TFSA] (MeO-C6H4-NH3 = 4-methoxyanilinium, TFSA = bis(trifluoromethanesulfonyl)ammonium) with the Aizu notation of mmmFm. Compared to the parent uniaxial ferroelectric [(MeO-C6H4-NH3)(18-crown-6)][BF4] with a Tc of 127 K, the introduction of larger TFSA anions brings a lower crystal symmetry at room temperature and a higher energy barrier of molecular motions in phase transition, giving [(MeO-C6H4-NH3)(18-crown-6)][TFSA] multiaxial ferroelectricity and a high Tc up to 415 K (above that of BaTiO3). To our knowledge, such a record temperature enhancement of 288 K makes its Tc the highest among the reported crown-ether-based ferroelectrics, giving a wide working temperature range for applications in data storage, temperature sensing, actuation, and so on. This work will provide guidance and inspiration for designing high-Tc host-guest inclusion ferroelectrics.